  January 29, 2010 - Hysitron is proud to announce the following published paper in Nature's January 2010 issue featuring in-situ TEM characterization using Hysitron's PI 95TM system.
Strong crystal size effect on deformation twinning
Qian Yu1, Zhi-Wei Shan1,2, Ju Li3, Xiaoxu Huang4, Lin Xiao1, Jun Sun1 & Evan Ma1,5
Nature 463, 335-338 (21 January 2010) | doi:10.1038/nature08692; Received 13 July 2009; Accepted 17 November 2009
Abstract
Deformation twinning in crystals is a highly coherent inelastic shearing process that controls the mechanical behaviour of many materials, but its origin and spatio-temporal features are shrouded in mystery. Using micro-compression and in situ nano-compression experiments, here we find that the stress required for deformation twinning increases drastically with decreasing sample size of a titanium alloy single crystal, until the sample size is reduced to one micrometre, below which the deformation twinning is entirely replaced by less correlated, ordinary dislocation plasticity. Accompanying the transition in deformation mechanism, the maximum flow stress of the submicrometre-sized pillars was observed to saturate at a value close to titanium's ideal strength. We develop a ‘stimulated slip' model to explain the strong size dependence of deformation twinning. The sample size in transition is relatively large and easily accessible in experiments, making our understanding of size dependence relevant for applications.
1. Center for Advancing Materials Performance from the Nanoscale (CAMP-Nano), State Key Laboratory for Mechanical Behavior of Materials, Xi'an Jiaotong University, Xi'an, 710049, China
2. Hysitron Incorporated, 10025 Valley View Road, Minneapolis, Minnesota 55344, USA 3. Department of Materials Science and Engineering, University of Pennsylvania, Philadelphia, Pennsylvania 19104, USA
4. Danish-Chinese Center for Nanometals, Materials Research Division, Risø National Laboratory for Sustainable Energy, Technical University of Denmark, DK-4000 Roskilde, Denmark
5. Department of Materials Science and Engineering, The Johns Hopkins University, Baltimore, Maryland 21218, USA
For further details on correspondence with the authors please visit Nature Journal's announcement webpage by clicking here. To contact a Hysitron representative regarding this please click here.
Source:
www.hysitron.com
|
.jpg)
info@microscopy-news.com
Top News / Archive
Home